Durlon® 8600
Durlon® 8600 is a quality compressed sheet gasket material for use in process industries including pulp & paper, power, petrochemical as well as general industry where a “white” gasket material is often required when working with food & beverage, pharmaceutical and plastics. Applications: water, steam, air, inert gases, alcohols, dilute acids and alkalis.
| Industries | Chemical Processing, Food & Beverage, General Industry, Mining, OEM Services |
|---|
A quality compressed sheet gasket material for use in process industries including pulp and paper, power, petrochemical as well as general industry where a “white” gasket material is often required such as food and beverage, pharmaceutical and plastics. For services such as water, steam, air inert gases, alcohols, dilute acids, alkalis ammonia and many other liquids and gases. Durlon® 8600 exhibits good compressibility and recovery, sealability, flexibility and cutting characteristics. A release agent on both sides ensures good anti-stick properties.
Durlon® 8600 contains high-strength aramid and inorganic fibres bonded with high-grade SBR rubber.
Color: White
Fiber: Aramid/Inorganic
Binder: SBR
Temperature:
Min: -100°F (-73°C)
Max: 700°F (371°C)
Continuous, max: 548°F (287°C)
Pressure, max: 1500 psi (103 bar)
Density: 106 lbs/ft3 (1.7 g/cc)
Compressibility: 8-16%
Recovery: 45%
Creep Relaxation: 20%
Tensile Strength: 1800 psi (12.4 MPa)
Sealability, cc/min ASTM F2378 (Nitrogen): 0.05
Sealability, ml/hr ASTM F37 (Fuel A): 0.03
Sealability, ml/hr ASTM F37 (Nitrogen): 0.5
Fluid Resistance - ASTM F146, IRM 903 oil, 5 hrs at 300°F (149°C)
Thickness Increase: 15-30%
Weight Increase: 30%
ASTM Fuel B 5 hrs at 70°F (21°C)
Thickness Increase: 5-20%
Weight Increase: 30%
Flexibility, ASTM F147: 8x
Volume Resistivity, ohm-cm, ASTM D257: 4.2 x 1013
Dielectric Breakdown, ASTM D149, kV/mm (V/mil): 11.7 (297)
Gasket Factors:
THICKNESS: 1/16"
m: 2.9
Y psi (MPa): 2540 (17.5)
Gb psi (MPa): 343 (2.4)
a: 0.325
Gs psi (MPa): 0.002 (0.3)
THICKNESS: 1/8"
m: N/A
Y psi (MPa): N/A
Gb psi (MPa): 866 (5.9)
a: 0.273
Gs psi (MPa): 37 (0.255)
Fiber: Aramid/Inorganic
Binder: SBR
Temperature:
Min: -100°F (-73°C)
Max: 700°F (371°C)
Continuous, max: 548°F (287°C)
Pressure, max: 1500 psi (103 bar)
Density: 106 lbs/ft3 (1.7 g/cc)
Compressibility: 8-16%
Recovery: 45%
Creep Relaxation: 20%
Tensile Strength: 1800 psi (12.4 MPa)
Sealability, cc/min ASTM F2378 (Nitrogen): 0.05
Sealability, ml/hr ASTM F37 (Fuel A): 0.03
Sealability, ml/hr ASTM F37 (Nitrogen): 0.5
Fluid Resistance - ASTM F146, IRM 903 oil, 5 hrs at 300°F (149°C)
Thickness Increase: 15-30%
Weight Increase: 30%
ASTM Fuel B 5 hrs at 70°F (21°C)
Thickness Increase: 5-20%
Weight Increase: 30%
Flexibility, ASTM F147: 8x
Volume Resistivity, ohm-cm, ASTM D257: 4.2 x 1013
Dielectric Breakdown, ASTM D149, kV/mm (V/mil): 11.7 (297)
Gasket Factors:
THICKNESS: 1/16"
m: 2.9
Y psi (MPa): 2540 (17.5)
Gb psi (MPa): 343 (2.4)
a: 0.325
Gs psi (MPa): 0.002 (0.3)
THICKNESS: 1/8"
m: N/A
Y psi (MPa): N/A
Gb psi (MPa): 866 (5.9)
a: 0.273
Gs psi (MPa): 37 (0.255)
Navy Adhesion Test, California Proposition 65, RoHS Reach Declaration